Sikadur®-300
2-Component, epoxy based impregnating resin.
Sikadur®-300 is a 2-component, epoxy based impregnating resin.
- Easy mix and application by trowel and impregnation roller
- Manufactured for manual or mechanical saturation methods
- Good adhesion to many substrates
- High mechanical properties
- Extra-long pot life
Usage
Sikadur®-300 is used as- Impregnating resin for SikaWrap® fabric reinforcement for the wet application method
- Primer resin for the wet application system
Advantages
- Easy mix and application by trowel and impregnation roller
- Manufactured for manual or mechanical saturation methods
- Good adhesion to many substrates
- High mechanical properties
- Extra-long pot life
Packaging
| 30 kg / set | (A+B) |
| 20 kg / set | (A+B) |
Colour
Component A: light-yellow to amber liquid
Component B: pale yellow to clear liquid
Components A + B mixed: light-yellow to clear liquid
Product Details
APPROVALS / STANDARDS
- Complies to Specification of Epoxy Adhesive for Bonding CFS, DPWH Item 416
- Complies to ASTM C881, Type I, Type IV, Grade 2
- Adhesive for structural bonding tested according to EN 1504-4, provided with the CE-mark
Chemical Base
Epoxy resin
Shelf Life
24 months from date of production
Storage Conditions
Store in original, unopened, sealed and undamaged packaging in dry conditions at temperatures between +5 °C and +30 °C. Protect from direct sunlight.
Density
| 1.16 kg/l (component A+B mixed) (at +23 °C) |
Viscosity
Shear rate: 50 /s
| Temperature | Viscosity |
+15 °C | ~2,000 mPas |
+23 °C | ~700 mPas |
| +40 °C | ~200 mPas |
System Structure
Substrate primer - Sikadur®-330 / Sikadur®-300.
Impregnating/laminating resin - Sikadur®-300.
Structural strengthening fabric - SikaWrap® type to suit requirements.
Compressive Strength
>50 MPa
Modulus of Elasticity in Flexure
| ~ 2,800 N/mm2 (7 days at +23 °C) | (DIN EN 1465) |
Tensile Strength
| ~ 45 N/mm2 (7 days at +23°C) | (ISO 527) |
Tensile Adhesion Strength
| Concrete fracture (> 4 N/mm2) on sandblasted substrate | (EN ISO 4624) |
Coefficient of Thermal Expansion
| 6.0 x 10−5 per °C (Temperature range −20 °C − +40 °C) | (EN 1770) |
Glass Transition Temperature
Curing time | Curing temperature | TG |
30 days | +30 °C | +53 °C |
Heat Deflection Temperature
Curing time | Curing temperature | HDT |
| 7 days | +15 °C | +43 °C |
| 7 days | +23 °C | +49 °C |
| 3 days | +40 °C | +60 °C |
| 7 days | +40 °C | +66 °C |
Resistant to continuous exposure +45 °C.
Service Temperature
–40 °C to +45 °C
Application
Mixing Ratio
Component A : component B = 100 : 34.5 by weight
When using bulk material the exact mixing ratio must be safeguarded by accurately weighing and dosing each component.
Ambient Air Temperature
+15 °C min. / +40 °C max.
Dew Point
Beware of condensation.
Substrate temperature during application must be at least 3 °C above dew point.
Substrate Temperature
+15 °C min. / +40 °C max.
Substrate Moisture Content
< 4 % pbw
Pot Life
Temperature | Potlife | Open time |
+15 °C | ~6 hours | ~3 hours |
+23 °C | ~4 hours | – |
| +40 °C | ~90 minutes | ~60 minutes |
The potlife begins when the resin and hardener are mixed. It is shorter at high temperatures and longer at low temperatures. The greater the quantity mixed, the shorter the potlife. To obtain longer workability at high temperatures, the mixed adhesive may be divided into portions. Another method is to chill components A+B before mixing them (not below +5 °C).
Consumption
See the "Method Statement for SikaWrap® manual wet application" Ref 850 41 03 and the "Method Statement for SikaWrap® saturator machine wet application" Ref 850 41 04.
depending on fabric type and method of application
SUBSTRATE QUALITY
The substrate must be sound and of sufficient tensile strength to provide a minimum pull off strength of 1.0 N/mm2 or as per the requirements of the design specification.
See also the "Method Statement for SikaWrap® manual wet application" Ref 850 41 03 and the "Method Statement for SikaWrap® saturator machine wet application" Ref 850 41 04.
SUBSTRATE PREPARATION
See the "Method Statement for SikaWrap® manual wet application" Ref 850 41 03 and the "Method Statement for SikaWrap® saturator machine wet application" Ref 850 41 04.
MIXING
Pre-batched units:
Mix components A+B together for at least 3 minutes at low speed. Avoid aeration while mixing. Then, pour the whole mix into a clean container and stir again for approx. 1 more minute at low speed to keep air entrapment at a minimum.
Bulk packing, not pre-batched:
Add the components in the correct proportions into a suitable mixing pail and stir correctly using an electric low speed mixer as above for pre-batched units.
CLEANING OF TOOLS
Clean all equipment immediately with Sika® Colma Cleaner. Cured material can only be removed mechanically.