Product Data Sheet Show all documents
Sikafloor®-264 HC
Sikafloor®-264 HC
Sikafloor®-264 HC
Sikafloor®-264 HC

Sikafloor®-264 HC

2- PART EPOXY ROLLER AND SEAL COAT

Sikafloor®-264 HC is a two part, coloured epoxy resin.

  • Good chemical and mechanical resistance
  • Easy application
  • Liquid proof
  • Gloss finish
  • Slip resistant surface possible
 
Product Data Sheet Show all documents

Usage

Sikafloor®-264 HC is used as:
  • Roller coat for concrete and cement screeds with normal up to medium heavy wear e.g. storage and assembly halls, maintenance workshops, garages and loading ramps.
  • Seal coat for broadcast systems, such as multi-storey and underground car parks, maintenance hangars and for wet process areas, e.g. beverage and food industry

Advantages

  • Good chemical and mechanical resistance
  • Easy application
  • Liquid proof
  • Gloss finish
  • Slip resistant surface possible
 

Packaging

20 kg set ready to mix units (Part A + B)

Part A :

15.8 kg containers

Part B :4.2 kg containers

Colour

Resin - part A :

coloured, liquid

Hardener - part B :transparent, liquid

Available in a number of colour shades. Please consult our Technical Sales Engineer for further details.
Under direct UV exposure (sun, lamp, skylight, etc.) there may be some discolouration and colour deviation, this has no influence on the function and performance of the coating.

Product Details

Sustainability / Certifications / Approvals

APPROVALS / STANDARDS

  • Particle emission certificate Sikafloor-264 HC CSM Statement of Qualification – ISO 14644-1, class 4– Report No. SI 0904-480 and GMP class A, Report No. SI 1008- 533.
  • Outgassing emission certificate Sikafloor-264 HC: CSM Statement of Qualification – ISO 14644-8, class 6,5 - Report No. SI 0904-480.
  • Good biological Resistance in accordance with ISO 846, CSM Report No. 1008-533
  • Fire classification in accordance with EN 13501-1, Re- port-No. 2013-B-2119/01, MPA Dresden, Germany, June 2013.
  • 2-part epoxy roller and seal coat according to EN 1504-2: 2004 and EN 13813:2002.
  • According to the EU-Directive 2004/42,           the maximum allowed content of VOC (Product category IIA / j type sb) is 550 / 500 g/l (Limits 2007 / 2010) for the ready to use product.
  • The maximum content of Sikafloor-264 is < 500 g/l VOC for the ready to use product
Product Information

Chemical Base

Epoxy

Shelf Life

24 months from the date of production

Storage Conditions

The product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +18 °C and +30 °C.

Density

Part A

~1.64 kg/L

Part B~1.00 kg/L
Mixed resin~1.40 kg/L

Solid content by weight

~100 %
Technical Information

Shore D Hardness

~76 (7 days / +23°C)

(DIN 53 505)

Abrasion Resistance

41 mg (CS 10/1000/1000) (8 days / +23°C)

(DIN 53 109)

Compressive Strength

~53 N/mm2 (Resin filled 1 : 0.9 with F36) (28 days / +23 °C)

(EN196-1)

Tensile Strength in Flexure

~20 N/mm2 (Resin filled 1 : 0.9 with F36) (28 days / +23 °C)

(EN 196-1)

Tensile Adhesion Strength

>1.5 N/mm2 (failure in concrete)

(ISO 4624)

Chemical Resistance

Resistance to many chemicals. Contact Sika Technical Service Department for specific information.

Thermal Resistance

Exposure*

Dry heat

Permanent+50 °C
Short-term max. 7 d+80 °C
Short-term max. 12 h+100 °C

Short-term moist/wet heat* up to +80 °C where exposure is only occasional (steam cleaning etc.).

Application

Application Information

Mixing Ratio

Part A : part B = 79 : 21 (by weight)

Ambient Air Temperature

+10 °C min. / +30 °C max.

Relative Air Humidity

80 % r.h. max.

Dew Point

Beware of condensation!
The substrate and uncured floor must be at least 3 °C above dew point to reduce the risk of condensation or blooming on the floor finish.
Note: Low temperatures and high humidity conditions increase the probability of blooming.

Substrate Temperature

+10 °C min. / +30 °C max.

Substrate Moisture Content

< 4 % pbw moisture content.
Test method: Sika®-Tramex meter, CM-measurement or Oven-dry-method. No rising moisture according to ASTM (Polyethylene-sheet).

Pot Life

Temperature

Time

+10 °C~50 min
+20 °C~25 min
+30 °C~15 min

Curing Time

Before applying Sikafloor®-264 HC on Sikafloor®-161 HC/-160 HC allow:

Substrate temperature

Minimum

Maximum

+10 °C

24 h

3 d

+20 °C12 h2 d
+30 °C8 h1 d

Before applying Sikafloor®-264 HC on Sikafloor®-264 HC allow:

Substrate temperature

Minimum

Maximum

+10 °C

30 h

3 d

+20 °C24 h2 d
+30 °C16 h1 d

Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.

Applied Product Ready for Use

Temperature

Foot traffic

Light traffic

Full cure

+10 °C~72 h~6 d~10 d
+20 °C~24 h~4 d~7 d
+30 °C~18 h~2 d~5 d

Note: Times are approximate and will be affected by changing ambient conditions.
Consumption

Consumption

Roller Coating:

Coating System

Product

Consumption

Primer

1-2 x Sikafloor®-161 HC/-160 HC

1-2 x 0.35-0.55 kg/m² for each layer

Top Coat

2 x Sikafloor®-264 HC

2 x 0.3 - 0.5 kg/m² for each layer

Textured Roller Coating:

Coating System

Product

Consumption

Primer

1-2 x Sikafloor®-161 HC/-160 HC

1-2 x 0.35-0.55 kg/m² for each layer

Top Coat

1-2 x Sikafloor®-264 HC + 1 % bw Extender T

1-2 x 0.5 - 0.8 kg/m² for each layer

Broadcast System ~4 mm :

Coating System

Product

Consumption

Primer

1 x Sikafloor®-161 HC/-160 HC

1 x 0.35-0.5 kg/m² for each layer

Wearing Course

1 pbw Sikafloor®-264 HC 1 pbw quartz sand (0.1 - 0.3 mm)

~4 kg/m2 (~2 kg/m2 binder + ~2 kg/m2 quartz sand

Broadcasting

Quartz sand 0.4 -0.7 mm

~4-6 kg/m2

Top Coat1-2 x Sikafloor®-264 HC1-2 x 0.6 - 0.8 kg/m² for each layer

These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level and wastage etc.
Application steps

MIXING

Prior to mixing stir part A mechanically. When all of part B has been added to part A, continuously mix for 3 minutes until a uniform mix has been achieved.
To ensure thorough mixing pour materials into another container and mix again to achieve a consistent mix.
Over mixing must be avoided to minimize air entrainment.


MIXING TOOLS


Sikafloor®-264 HC must be thoroughly mixed using a low speed electric stirrer (300 - 400 rpm) or other suitable equipment. For the preparation of mortars use a forced action mixer of rotating pan, paddle or trough type. Free fall mixers should not be used.

APPLICATION

Prior to application, confirm substrate moisture content, relative air humidity and dew point. If > 4 % pbw moisture content, Sikafloor® EpoCem® may be applied as a T.M.B. (temporary moisture barrier) system.

 

Primer

Make sure that a continuous, pore free coat covers the substrate. If necessary, apply two priming coats. Apply Sikafloor®-161 HC/-160 HC by brush, roller or squeegee. Preferred application is by using a squeegee and then backrolling crosswise.

Levelling

Rough surfaces need to be levelled first. Therefore use e.g. Sikafloor®-161 HC levelling mortar (see PDS).

Coating

Sikafloor®-264 HC as coating, can be applied by short-piled roller (crosswise).

Seal Coat

Sealer coats can be applied by squeegee and then back-rolled (crosswise) with a short-piled roller.

CLEANING OF TOOLS

Clean all tools and application equipment with Thinner C immediately after use. Hardened and/or cured material can only be removed mechanically.