Product Data Sheet Show all documents
Sika® ViscoCrete®-4100

Sika® ViscoCrete®-4100

High-efficient superplasticizer Powered by ViscoCrete®

Sika® ViscoCrete®-4100 is the latest development superplasticizer for concrete. It meets the requirements for high range water reducing superplasticizers according to ASTM 494 Type F.

Sika® ViscoCrete®-4100 is a powerful superplasticizer based on advanced technology which gives the following advantages:
  • Strong water reduction, resulting in high density, high strength and reduced permeability
  • Less sensitive against variations in aggregates and / or different cement types
  • High efficiency even at low dosage rates
  • Extended workability in conjunction with subsequent strength development
  • Superior plasticizing effect, resulting in improved flow, placing and compaction characteristics
  • Reduced shrinkage during curing and reduced creep when hardened
  • Provides many opportunities for cost improvement e.g.:
  • Cement replacement/reduction
  • More economic mix design
Sika® ViscoCrete®-4100 does not contain chloride or any other ingredients which promote the corrosion of steel. It is therefore suitable for use in reinforced and prestressed concrete structures.
Product Data Sheet Show all documents

Usage

Sika® ViscoCrete®-4100 is a unique multi-purpose      superplasticizer that is particularly suitable for the production of ready-mixed concrete. Additionally it provides high water reduction and improved fresh concrete characteristics. With its outstanding cost/performance Sika® ViscoCrete®-4100 is used for the following:
  • A wide range of application where excellent
   workability is requested
  • Concrete with high water reduction
  • High efficient concrete applications
  • Variable use in different concrete systems with different raw materials
 

Advantages

Sika® ViscoCrete®-4100 is a powerful superplasticizer based on advanced technology which gives the following advantages:
  • Strong water reduction, resulting in high density, high strength and reduced permeability
  • Less sensitive against variations in aggregates and / or different cement types
  • High efficiency even at low dosage rates
  • Extended workability in conjunction with subsequent strength development
  • Superior plasticizing effect, resulting in improved flow, placing and compaction characteristics
  • Reduced shrinkage during curing and reduced creep when hardened
  • Provides many opportunities for cost improvement e.g.:
  • Cement replacement/reduction
  • More economic mix design
Sika® ViscoCrete®-4100 does not contain chloride or any other ingredients which promote the corrosion of steel. It is therefore suitable for use in reinforced and prestressed concrete structures.

Packaging

210 liter Drum, 1000 liter Bulk

Colour

Clear to slight yellowish

Product Details

Product Information

Chemical Base

Polycarboxylate ether

Shelf Life

12 months from date of production if stored properly

Storage Conditions

Store properly in undamaged, unopened, original sealed packaging, in dry conditions at temperatures between +5°C and +30°C. Protect from direct sunlight.

Specific Gravity

1.05 ± 0.03 kg/L

Application

Application Information

Dispensing

Sika® ViscoCrete®-4100 is added to the gauging water or added with it into the concrete mixer. To take advantage of the high water reduction, a wet mixing time, which is depending on the mixing conditions and mixer performance, of at least 60 seconds is recommended. To avoid excess water in the concrete, the final dosage must begin only after 2/3 of the wet mixing time.

Notes on application / Limitations
When using Sika® ViscoCrete®-4100a suitable mix design has to be taken into account and local material sources shall be subjected to trial. Sika® ViscoCrete®-4100 shall not be added to dry cement.
Consumption

Recommended Dosage

0.6% - 2.0% by weight of total cementitious binder
Application steps

APPLICATION INSTRUCTIONS

Application method / Tools
The standard rules of good concreting practice, concerning production and placing, are to be followed. Laboratory trials shall be carried out before concreting on site, especially when using a new mix design or producing new concrete components. Fresh concrete must be cured properly and curing applied as early as possible.


Cleaning of tools
Clean all tools and application equipment with water immediately after use. Hardened / cured material can only be removed mechanically.