Sikafloor®-82 EpoCem®
Sikafloor®-82 EpoCem® is a three part, epoxy modified cementitious, fine textured mortar for self-smoothing floor screeds in layers of 3 to 7 mm.
- Can be over coated with resin based floors after 24 hours (+20ºC, 75% r.h.)
- Prevents osmotic blistering of resin based coatings over damp substrates
- Easy application
- Good levelling properties
- Impervious to liquids but permeable to water vapour
- Compatible with bituminous overlays
- Good chemical resistance
- Thermal expansion properties similar to concrete
- Excellent bond to green or hardened concrete whether damp or dry
- Excellent early and final mechanical strengths
- Excellent resistance to water and oils
- It is the ideal preparation for smooth surface finishes
Usage
As a Temporary Moisture Barrier (TMB) (3-7 mm thick) allowing the application of Epoxy, Polyurethane and PMMA* resin floors requiring dry substrates, over high moisture content substrates, even green concrete, for a lasting solution. As a self-smoothing screed for:- Levelling or patching horizontal concrete surfaces, in new work or repairs, in aggressive chemical environments
- Floor topping on non-ventilated damp substrates without particular aesthetic requirements
- Levelling layer under Epoxy, Polyurethane and PMMA* floor coatings / screeds, tiles, sheet floors, carpets or wooden floors
- Repair and maintenance of monolithic and vacuum concrete floors
Advantages
- Can be over coated with resin based floors after 24 hours (+20ºC, 75% r.h.)
- Prevents osmotic blistering of resin based coatings over damp substrates
- Easy application
- Good levelling properties
- Impervious to liquids but permeable to water vapour
- Compatible with bituminous overlays
- Good chemical resistance
- Thermal expansion properties similar to concrete
- Excellent bond to green or hardened concrete whether damp or dry
- Excellent early and final mechanical strengths
- Excellent resistance to water and oils
- It is the ideal preparation for smooth surface finishes
Packaging
Pre-batched 31 kg units.
| Part A | 1.14 kg plastic container |
| Part B | 2.86 kg plastic container |
| Part C | 27 kg / plastic bag |
Colour
Part A-resin: | white liquid |
| Part B - hardener | transparent yellow liquid |
| Part C - filler: | natural grey aggregate powder |
| Colour: | light grey |
| Finish Colour: | Matt grey |
Product Details
APPROVALS / STANDARDS
- Test report, Ref. 04 1706 dated 29/11/2004 by MPA Dresden GmbH. Fire rating.
- Epoxy modified cementitious mortar for self-smoothing floor screeds according to EN 1504-2: 2004 , EN 1504-3: 2005 and EN 13813:2002, DoP 02 08 02 01 002 0 000001 1001 , certified by Factory Production Control Body No. 2116 and provided with the CE-mark
Chemical Base
Epoxy modified cementitious mortar.
Shelf Life
| Part A, part B: | 12 months |
| Part C: | 9 months |
Storage Conditions
The product must be stored in original, unopened and undamaged sealed packaging, in dry conditions at temperatures between +5°C and +30°C.
Part A, part B: | Protect from frost |
| Part C: | Protect from humidity |
Density
| Part A | ~1.05 kg/l (at +20°C) |
Part B | ~1.03 kg/l (at +20°C) |
Mixed resin | ~1.97 kg/l (at +20°C) |
| Mixed A+B+C: | ~2.10 kg/l (at +20°C) |
Compressive Strength
| +23ºC / 50% r.h. | |
1 day | ≥ 15 N/mm2 |
28 days | ≥ 45 N/mm2 |
Tensile Strength in Flexure
| +23ºC / 50% r.h. | |
1 day | ≥ 2 N/mm2 |
28 days | ≥ 10 N/mm2 |
Freeze Thaw De-Icing Salt Resistance
Resistance factor WFT-L 86% (High) | D-R (SN / VSS 640 461) |
Carbonation Resistance
Carbonation resistance for 8 mm thickness: R ≈ 24.2 m
Application
Mixing Ratio
Part A : part B : part C - packing size : 1.14 : 2.86 : 25 kg
Flooring Screed:
At temperatures between +12ºC to +25ºC:
1 : 2.5 : 21.9 (by weight)
Parts (A+B) : C = 4 kg : 25 kg
At temperatures between +8ºC to +12ºC and +25ºC to +30ºC:
The amount of part C can be reduced to 24 kg in order to improve workability.
Please note:
Never reduce part C by more than this amount.
1 : 2.5 : 21 (by weight)
Parts (A+B) : C = 4 kg : 24 kg
For this application, to achieve a good bond of the mortar to the substrate,
SikaTop®-Armatec®-110 EpoCem® must be used as a primer. Apply the mortar wet on wet to the primer.
Ambient Air Temperature
+8°C min. / +30°C max.
Layer Thickness
3.0 mm minimum / 7.0 mm maximum
If Sikafloor®-82 EpoCem® is used as a Temporary Moisture Barrier (TMB), a minimum of 3 mm must be applied.
Relative Air Humidity
20% min. / 80% max.
Substrate Temperature
+8°C min. / +30°C max.
Substrate Moisture Content
Can be applied on green or damp concrete, without any standing water.
Although the product can be applied onto green concrete surfaces (> 24 hours), it is advised to allow at least 3 days for early shrinkage of concrete to occur in order to prevent concrete shrinkage cracks from appearing on the screed surface.
Pot Life
Temperature / R.H 75% | Time |
+10°C | ~50 minutes |
+20°C | ~25 minutes |
| +30°C | ~12 minutes |
29 kg units
Curing Time
Once Sikafloor®-82 EpoCem® is tack free it is possible to apply vapour permeable seal coats.
For the application of vapour tight coatings on Sikafloor®-82 EpoCem®, allow the surface moisture to fall below 4%, not earlier than:
Substrate Temperature | Waiting Time |
+10°C | ~3 days |
+20°C | ~1 day |
| +30°C | ~1 day |
Consumption
Primer:
Sikafloor® Repair Module HC (parts A+B), thinned with 10% water, ~0.3 - 0.5 kg/m2 dependent on the substrate conditions, when repairing monolithic or vacuum concrete, or without a broadcast finish or when Sikafloor®-82 EpoCem® is over-coated with itself.
Self smoothing screed:
Sikafloor®-82 EpoCem® ~2.25 kg/m2/mm
~6.75 kg/m2 for a 3 mm thick application (minimum for T.M.B.).
These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level or wastage, etc.
MIXING
Prior to mixing, shake part A (white liquid) briefly until homogenous, then pour into container of part B and shake vigorously again for at least 30 seconds. When dosing out of drums, stir and homogenise first.
Pour the mixed binder mixture (A+B) into a suitable mixing container (capacity of about 30 litres) and gradually add part C to the mixer while stirring with a power mixer. Mix thoroughly for 3 minutes until a uniform mix has been achieved with no lumps.
Mix only full units of A+B+C components. Do not mix smaller amounts. Do not add water.
When dosing with additional aggregates, add them after adding part C to the mix. Mix thoroughly for 3 minutes until a uniform mix has been achieved.
Mixing Tools:
Mix using a slow speed electric mixer (300 - 400 rpm) with helical paddle or other suitable equipment.
For mixing 2 – 3 bags at once, single or counter rotating double mortar (basket type) and forced action (pan type) mixers are also recommended. Free fall mixers must not be used.
APPLICATION
Place mixed Sikafloor®-82 EpoCem® onto the primed substrate and spread evenly to the required thickness uniformly with a rubber or metal trowel or spatula to and immediately roll with a spike roller to remove entrapped air and obtain an even thickness layer.
Workability can be adjusted by varying slightly the amount of Part C.
See Mixing above
Do not use additional water, which would disturb the surface finish and cause discolouration.
A seamless finish can be achieved if a “wet” edge is maintained during application.
CLEANING OF TOOLS
Clean all tools and application equipment with water immediately after use. Hardened / cured material can only be removed mechanically.